Cr4+:YAG Crystal is an excellent crystal for passively Q-switching diode pumped or lamp-pumped Nd:YAG, Nd:YLF, Nd:YVO4 or other Nd and Yb doped lasers at wavelength from 0.8 to 1.2 m. Because of its c..
Cr4+:YAG Crystal is an excellent crystal for passively Q-switching diode pumped or lamp-pumped Nd:YAG, Nd:YLF, Nd:YVO4 or other Nd and Yb doped lasers at wavelength from 0.8 to 1.2 µm. Because of its chemically stable, durable, UV resistant, good thermal conductivity and high damage threshold (> 500 MW/cm2) and being easy to be operated, it will replace traditional materials, such as LiF, organic Dye and color centers.
Chemical Formula
|
Cr4+:Y3Al5O12
|
Crystal Structure
|
Cubic garnet
|
Recovery time
|
8.5 μs
|
Hardness
|
8.5 Mohs
|
Density
|
4.56 g/cm3
|
Thermal conductivity
|
12.13 W/m/K
|
Refractive index
|
1.82 @ 1064nm
|
Ground state absorption cross section
|
σs1=4.3x10-18cm2
|
Excited state absorption cross section
|
σs2=8.2x10-19cm2
|
Fluorescence lifetime
|
3.4 μs
|
Orientation:
|
The rod axis is along [100] within5°,[111] and [110] within5°
|
Cr4+ concentration:
|
0.5 mol% ~ 3 mol%
|
Aperture
|
2x2 ~ 20x20 mm
|
Length:
|
0.1 ~ 12 mm
|
Initial transmission:
|
5% ~ 99%
|
Angle tolerance:
|
Δθ< ± 0.5°; Δφ< ±0.5°
|
Flatness:
|
λ /8 @ 633 nm
|
Parallelism:
|
20 arc sec
|
Perpendicularity:
|
5 arc minutes
|
Surface finishing:
|
20/10 scratch/dig to MIL-O-13830A
|
Wavefront distortion:
|
less than λ/8 @ 633 nm
|
Coating
|
AR/HR/PR coating upon customer’s request
|