Description: The magneto-optical crystal TGG crystal is an optimum material for Faraday devices (Rotator and Isolator) in the wavelength range 400 nm-1100 nm, excluding 470-500 nm. TGG crystal has a ..
Description:
Chemical Formula
|
Tb3Ga5O12
|
Lattice Parameter
|
a=12.355Å
|
Density
|
7.13 g/cm3
|
Mohs Hardness
|
8
|
Melting Point
|
1725 ℃
|
Refractive Index
|
1.954 @ 1064 nm
|
Thermal Conductivity
|
9.4 x 10-6C-1
|
Verdet Constant
|
0.12 min/Oe.cm @ 1064 nm
|
Orientation
|
[111] within ±15 arc min
|
Wave Front Distortion
|
< λ/8 wave
|
Extinction Ratio
|
> 30dB
|
Diameter
|
+0.00mm/-0.05mm
|
Length
|
+0.2mm/-0.2mm
|
Chamfer
|
0.10mm @ 45°
|
Flatness
|
< λ/10 wave @ 633nm
|
Parallelism
|
< 30 arc Seconds
|
Perpendicularity
|
< 5 arc min
|
Surface Quality
|
10/5 Scratch/Dig
|
Coating
|
upon customer's request
|